Study of corrosive process and life prospect of API 5L X70 steel with and without niobium coating on chemically treated soil

Fernanda Menezes França, Gustavo Victor Souza, Fabrícia Nunes de Jesus Guedes

Abstract


The diversity of the employment of steel corroborates its great importance to society. Due to its versatility and wide field of operation, steel can be used submerged in the ground in the construction of extensive pipelines, pipelines and tanks to transport fuel. The constant contact between the steel pipe and the soil, over time, renders it exposed to corrosive action. As a result, high direct costs are involved with inspection, maintenance and replacement of parts, and indirect costs due to health problems resulting in contamination, depletion of mineral resources, perforations with loss of materials, besides environmental damages. The study of corrosive processes has grown greatly and the knowledge of both the principles of corrosion and corrosion protection is essential in the search for solutions to mitigate the effects of corrosion, to prevent their occurrence and develop materials with a better resistance. API 5L X70 steels are used in pipelines that transports gas, oil and its derivatives where high mechanical and corrosion resistance are required. In this way, these steels are susceptible to the corrosive process, since they are in direct contact with diverse Brazilian soils and environments. In the present work, the behavior of API 5L X70 steel with and without niobium coating was evaluated in soil chemically treated with acid solutions (simulating acid rain) and basic (simulating soil liming). Techniques such as thermal spraying (for sample coating), experimental corrosion tests and scanning electron microscopy were used in order to identify the corrosion products. At the end, the forms and types of corrosion obtained in the test specimens were classified, the corrosion rate was calculated and the efficiency and the technical feasibility of the niobium coating were evaluated in addition to their anticorrosive properties.


Keywords


Corrosion, Coating, Steel API 5L X70, Niobium, Soil.

References


Alves, A. R.; Coutinho, A. R.(2015). The Evolution of the Niobium Production in Brazil. Materials Research, v. 18, n. 1, p. 106-112.

American Society For Testing And Materials - ASTM.(2017). Standard Practice for Preparing, Designation G1-90/ G1-03, Cleaning, and Evaluation Corrosion Test Specimens, Pennsylvania.

Associação Brasileira de Normas Técnicas.(1986) ABNT NBR 6457: Amostras de Solos – Preparação para ensaios de compactação e caracterização. Rio de Janeiro/RJ.

Associação Brasileira de Normas Técnicas.(1986) ABNT NBR 7348:2017 Pintura industrial – Preparação de superfície de aço com jateamento abrasivo ou hidrojateamento. Rio de Janeiro/RJ.

Callister, Jr.(2008). Ciência, W. D. engenharia dos materiais uma introdução, 7ª edição. Rio de Janeiro: LTC.

Gentil, V. (2007). Corrosão. 3. ed. Rio de Janeiro: LTC.

Mariano, C.; Paredes, R.S.C; Frare JR, A. F.(2007). Desenvolvimento de Revestimentos de Nióbio Resistentes a Elevadas Temperaturas Depositados por Aspersão Térmica. 4º PDPETRO, Campinas, SP, pp.2.4.0305-1 -2.

Martins, J. I. F. P. A corrosão: a outra perspectiva de abordagem. Corrosão e Proteção de Materiais, v. 31, n. 59, 2012.

Metallisation. (2017). An introduction to metal spray for corrosion protection | Applications | Metallisation Ltd. Retirado no dia 17 de novembro, de https://metallisation.com/applications/an-introduction-to-metal-spray-for-corrosionprotection-application/

National Association Of Corrosion Engineers – NACE.(1999). NORMA RP-0775. Standard recommended practice, preparation, installation, analysis and interpretation of corrosion coupons in oilfield operations.




DOI: http://dx.doi.org/10.33448/rsd-v8i9.1238

Refbacks

  • There are currently no refbacks.


Base de Dados e Indexadores: Base, Diadorim, Sumarios.org, DOI Crossref, Dialnet, Scholar Google, Redib, Doaj, Latindex, Redalyc, Portal de Periódicos CAPES

Research, Society and Development - ISSN 2525-3409

Licença Creative Commons
Este obra está licenciado com uma Licença Creative Commons Atribuição 4.0 Internacional

Rua Irmã Ivone Drumond, 200 - Distrito Industrial II, Itabira - MG, 35903-087 (Brasil) 
E-mail: rsd.articles@gmail.com
Facebook: https://www.facebook.com/Research-Society-and-Development-563420457493356